Flint Clay, Refractory Products, Refractory Materials manufacturer / supplier in China, offering Calcined Flint Clay for Fire Bricks, Alumina Zirconia Ceramic Fibre Paper-1400 High Alumina for Boiler and Furnace, Alumina - Silicate Ceramic Fiber Blanket for Boiler Insulation and so on.

(/ )

Supplier Homepage Product Refractory Calcined Flint Clay for Fire Bricks

Calcined Flint Clay for Fire Bricks

FOB Price: US $150 / Ton
Min. Order: 1 Ton
Min. Order FOB Price
1 Ton US $150/ Ton
Get Latest Price
Production Capacity: 5000 Ton/Tons Per Month
Transport Package: Wooden Pallet with 25kg Jumbo Bag
Payment Terms: L/C, T/T, Western Union, Money Gram

Request a custom order and have something just for you!

Send Customized Request
Basic Info
  • Model NO.: YH Flint Clay
  • Feature: Long Time Materials
  • Shape: Block
  • Al2O3 Content (%): 44%,45%,46%
  • Whiteness: 90
  • Bulk Density: 2.45-2.58g/Cm³
  • Technique: Calcined Kaolin
  • Specification: SGS, CE
  • Refractoriness (℃): 1580< Refractoriness< 1770
  • Type: Refractory Material
  • Material: Alumina Block
  • Sio2 Content (%): 49-54
  • Fe2o3 Content (%): 0.8-2.5
  • Dimensions: 0-1,1-3,3-5,5-8
  • Trademark: YH
  • Origin: Zibo, Shandong, China
Product Description
Flint Clay Industrial Clay Refractory Material
 
Flint Clay 
Product Description
Flint Clay is a kind of high quality hard refractory clay
origin from Zibo in Shandong Province, China. Standard flint clay ore
Al2O3 content is 38%,Al2O3 content is about 44% after calcined, Fe2O3 < 2%. 
Stable composition, uniform texture,compact structure, cross section
assumes the shells, white, used in the production of high quality clay 
refractory materials.

The Jargon of Flint Clay is the the first level hard clay grog, main 
chemical composition is SiO2 and AL2O3, accompanied by a small 
amount of Fe2O3 and trace Na2O, K2O, main mineral is kaolinite.
 
Specification 
and Test Index

Chemical composition is stable, export level generally as follows:
(1) Al2O3: not less than 44%; Fe2O3: no more than 1.5%;
B.D. : not less than 2.45 g/cm³;
(2) Al2O3: not less than 45%; Fe2O3:no more than 1.2%;
B.D. : not less than 2.50 g/cm³; 
(3) Al2O3: not less than 46%; Fe2O3: no more than 1.2%;
B.D. : not less than 2.55 ~ 2.58 g/cm³; 
 In Additoon:K2O + Na2O + CaO + MgO : below0.5 ~ 1.0%.
 
Purpose of the
 chamotte and origin:
 

Market research shows that the composition and ingredient of the chamotte
are complicated, no fixed structure and composition. The chamotte not easily
dispersed in water, low plasticity. Known in China at present the chamotte 
for kaolinite clay mineral deposits. Sometimes there are associated with 
dickite and hydromica etc. mineral. The SiO2 and Al2O3 content ranges are
 small. From the chemical composition, it is close to the theory of composition 
of kaolinite (Al2O3 /3SiO2 = 0.85).In addition to the free silica, a small amount 
of iron ore and alkali metal oxide constitute the impurities.
The common colors of high temperature calcined chamotte contain white,
 light gray, yellowish brown, there is a small amount of brown metal material.
The chamotte is of good heat resistance and sintering.
The chamotte is of good heat resistance and sintering.
The chamotte is a mixture containing a variety of aluminum silicate.
 Main chemical composition is SiO2 and Al2O3, impurities are mainly alkali, 
alkaline earth and iron and titanium oxide, and some organic matter. 
Various oxides  helps fusion, can reduce refractoriness of the materials. 
As a result, the impurity content in the chamotte, especially Na2O + K2O
content is lower, the higher refractoriness. And the closer to the theoretical
value Al2O3 /3SiO2 ratio (A/S = 0.85), that indicates the chamotte is higher 
purity. A/S more bigger, flint clay refractoriness is higher, the sinter melting
range will be wide. The chamotte refractoriness with high quality can reach
more than 1750 ºC.
The chamotte after high temperature calcination has a small volume stability,
strength and water absorption properties. To measure the degree of the
chamotte sintering indexes generally have true density, bulk density, porosity
, water absorption, firing shrinkage rate, etc. Good sintering degree the 
chamotte bibulous rate is less than 5%, the volume density is greater than
 2.55 g/cm³. 
 
Origin:
The mainly origin of the chamotte is shandong province. Especially in
Wangcun village,the quality is better,the chamotte whiteness and luminosity
 are good, and they are magnetic. 

Purpose:
Used in the production of highgrade refractory materials, manufacturing 
ceramic, aluminum silicate refractory fiber production and military industry, 
etc. 
Packaging & Shipping 

The products are packed by wooden pallet with 25kg jumbo bag or as
 requirements.
 
Send your message to this supplier
Avatar
Ms. Angela Wang
Sales Manager
*From:
To: Ms. Angela Wang
*Message:

Enter between 20 to 4,000 characters.

This is not what you are looking for? Post a Sourcing Request Now